Please use this identifier to cite or link to this item: http://dspace.sctimst.ac.in/jspui/handle/123456789/583
Full metadata record
DC FieldValueLanguage
dc.contributorSailaja, G. S.-
dc.contributorRamesh, P.-
dc.contributorVarma, H. K.-
dc.date.accessioned2012-12-04T11:44:16Z-
dc.date.available2012-12-04T11:44:16Z-
dc.date.issued2007-
dc.identifier.citationJOURNAL OF BIOMEDICAL MATERIALS RESEARCH PART B-APPLIED BIOMATERIALS. 82B; 1; 231-238en_US
dc.identifier.urihttp://dx.doi.org/10.1002/jbm.b.30725-
dc.identifier.urihttp://onlinelibrary.wiley.com/doi/10.1002/jbm.b.30725/full-
dc.identifier.urihttp://dspace.sctimst.ac.in/jspui/handle/123456789/583-
dc.description.abstractA simple but efficient processing method for shaping intricate bioceramic green bodies has been developed by using natural rubber latex as binder. Different shapes of hydroxyapatite Ca-10(PO4)(6)(OH)(2) (HAP) were molded from a composite formulation containing wet precipitated HAP, natural rubber latex (NRL), and a stabilizer. On controlled heat treatment followed by sintering, dense shapes of HAP contours were obtained. The thermal degradation profile of HAP-NRL composites shows that NRL degrades slowly without any abrupt exotherm. The results of energy dispersive X-ray analysis together with inductively coupled plasma (ICP) analysis indicate that the inorganic residue of NRL does not contain any heavy element. The sintered density of the samples increased with increased HAP content in the formulation and percentage shrinkage reduced accordingly. On varying the HAP content in the formulation from 35 to 95 wt %, the compositions with 85, 90, 92, and 95 wt % HAP showed better flexural strength in the range 40-54 MPa and a flexural modulus value in the range 36-50 GPa. The fracture morphology, as observed by the scanning electron microscope confirms that with increased HAP content in the formulation the sample microstructure attains higher uniformity. The Vickers microhardness for the samples sintered at two different temperatures (1150 and 1250 degrees C) showed that hardness increases with increase in the sintering temperature with a maximum for the highest HAP loaded formulation. (c) 2006 Wiley Periodicals. Inc.-
dc.publisherJOURNAL OF BIOMEDICAL MATERIALS RESEARCH PART B-APPLIED BIOMATERIALS-
dc.subjectBiomaterials-
dc.titleHydroxyapatite moldable formulation using natural rubber latex as binder-