Title: Polyurethanes with radiopaque properties
Authors: James, NR
Philip, J
Jayakrishnan, A
Keywords: Biomaterials
Issue Date: 2006
Publisher: BIOMATERIALS
Citation: BIOMATERIALS. 27; 2; 160-166
Abstract: An aliphatic, commercially available, medical grade polyurethane, Tecoflex 80 A was made radiopaque by coupling a 5-iodine-containing molecule, N-(2,6- diiodocarboxyphenyl)-3,4,5-triiodo benzamide (DCPTB) onto the polymer backbone. DCPTB was synthesized by coupling 4-ainino-3,5-diiodobenzoic acid and 3,4,5-triiodobenzoic acid using dicyclohexyl carbodiimide. Radiopaque polyurethane thus obtained was characterized by IR, TGA, DSC and X-radiography. By optimizing the reaction conditions, it was possible to incorporate about 8% iodine in the polymer (wt/wt) to achieve radiopacity almost equivalent to that of a 2mm thick aluminium wedge. However, the products differed from the starting polymer in thermal characteristics. The starting polymer showed two endothermic transitions, the first one due to glass transition of the soft segment and the second one due to disruption of the hard segments. After modification, the second transition shifted to a lower temperature, while the first transition remained unaltered. Also, the modified polymers showed reduced thermal stability compared to the starting polymer. These observations could be explained on the basis of the reduced extent of intermolecular hydrogen bonding among the hard segments of the end product. Radiopaque polyurethanes are expected to have significant advantage over their non-radiopaque counterparts in many medical and related applications. (c) 2005 Elsevier Ltd. All rights reserved.
URI: http://dx.doi.org/10.1016/j.biomaterials.2005.05.099
http://dspace.sctimst.ac.in/jspui/handle/123456789/888
Appears in Collections:Journal Articles

Files in This Item:
There are no files associated with this item.


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.