  • Item
    A new generation of high flex life polyurethane urea for polymer heart valve-Studies on in vivo biocompatibility and biodurability
    (JOURNAL OF BIOMEDICAL MATERIALS RESEARCH PART A, 2009)
    Development of new generation high flex life polyurethane urea (HFL18-PU) with appropriate elastic modulus, biocompatibility, blood compatibility, resistant to calcification, and biodurability for the long-term use as cardiac device is still a challenge. This study reports the development of a fully aliphatic, ether-free physically cross-linked and low elastic modulus (6.841 +/- 0.27 MPa) polyurethane urea having hi vivo biostability, in vivo biocompatibility and high flex-life (721 +/- 30 million cycles) that can satisfy the requirements for the fabrication of tri-leaflet heart valve. (c) 2008 Wiley Periodicals, Inc. J Biomed Mater Res 89A: 192-205, 2009
  • Item
    Development of segmented polyurethane elastomers with low iodine content exhibiting radiopacity and blood compatibility.
    (Biomedical materials (Bristol, England), 2011)
    Biofunctionally active and inherently radiopaque polymers are the emerging need for biomedical applications. Novel segmented polyurethane elastomer with inherent radiopacity was prepared using aliphatic chain extender 2,3-diiodo-2-butene-1,4-diol, polyol polytetramethylene glycol and 4,4'-methylenebis(phenyl isocyanate) (MDI) for blood compatible applications. Aliphatic polyurethane was also prepared using hexamethylene diisocyanate for comparison. X-ray analysis of the polyurethanes revealed good radiopacity even at a relatively low concentration of 3% iodine in aromatic polyurethane and 10% in aliphatic polyurethane. The polyurethanes also possessed excellent thermal stability. MDI-based polyurethane showed considerably higher tensile strength than the analogous HDI-based polyurethane. MDI-based aromatic polyurethane exhibited a dynamic surface morphology in aqueous medium, resulting in the segregation of hydrophilic domains which was more conducive to anti-thrombogenic properties. The polyurethane was cytocompatible with L929 fibroblast cells, non-hemolytic, and possessed good blood compatibility.
  • Item
    Synthesis and characterization of biodegradable poly (ethylene glycol) and poly (caprolactone diol) end capped poly (propylene fumarate) cross linked amphiphilic hydrogel as tissue engineering scaffold material.
    (Journal of materials science. Materials in medicine, 2009)
    Biodegradable poly (caprolactone diol-co-propylene fumarate-co-ethylene glycol) amphiphilic polymer with poly (ethylene glycol) and poly (caprolactone diol) chain ends (PCL-PPF-PEG) was prepared. PCL-PPF-PEG undergoes fast setting with acrylamide (aqueous solution) by free radical polymerization and produces a crosslinked hydrogel. The cross linked and freeze-dried amphiphilic material has porous and interconnected network. It undergoes higher degree of swelling and water absorption to form hydrogel with hydrophilic and hydrophobic domains at the surface and appreciable tensile strength. The present hydrogel is compatible with L929 fibroblast cells. PCL-PPF-PEG/acrylamide hydrogel is a candidate scaffold material for tissue engineering applications.